The waste of ceramic handicrafts in Klampok Subdistrict, Banjarnegara Regency have not been widely used. Ceramic waste if crushed has similarities to fine aggregates (pass the 0.15mm filter). This research is an experimental study to determine the compressive strength of concrete using cylindrical specimens with a diameter of 15cm and a height of 30cm for normal concrete and a mixture of ceramic craft waste with variations of 5%, 10%, 15%, and 20%. Testing of compressive strength in concrete was carried out at 28 days with a compressive strength of 21.7 Mpa. The results showed that the higher the value of mixed proportions (20%), the lower the compressive strength produced was 15.4 Mpa. As for the slump value, the more mixed proportions of ceramic craft waste on concrete the higher the slump value will be and the lighter the concrete will produce.